Recoflex
Product Details
Product Data
|
Specific weight |
approx. 440 kg/m³ |
|
Delivery format |
sheets |
| Dimension |
2.500 x 1.250 mm (Standard) |
| Colour | nature, other RAL-colours possible |
Product Specification
|
Emission values |
According to emission tests performed by LGA Qualitest GmbH, Nürnberg, |
|
|
Formaldehyde emission |
0.005 ppm |
Permissible maximum value for wood material (E1) according to chemical prohibition law = 0.1 ppm Legal requirements fulfilled. |
|
Effects on formaldehyde emission in composite material |
It is now possible to laminate fewer panels to another while maintaining the same thickness of the molded part, with Recoflex core. This additionally reduces the formaldehyde emission when 2-component glues containing formaldehyde are used by reducing the quantity of glue. |
|
|
Emission of volatile organic compounds |
CMT substances, all < 1 µg/m³ |
Legal requirements fulfilled (RAL-UZ 38). |
|
|
|
|
|
Combustion characteristics |
according to test performed by Siemens AG, A&D SP, Report 2004-1776 |
E DIN 5510-2: 2003-9 |
|
Fire classification |
B 2 |
DIN 4102 |
|
Heat conductivity |
according to MFPA, Weimar, DIN 52612-1:1979-09 At 10 average temperature ë10 = 0.0836 W/mK temperature difference on surface of two outer size: 10.2°C |
Heat conductivity Styrene 0.03 Wood 0.13 Concrete 1.40 |
|
Heat transmission resistance |
1/Ë = 0.19 m²K/W |
Volume change in water after 72 hours
(Own test BSW)
|
Material: |
Thickness at start |
Thickness after 72 hours |
Thickness in % |
Increase in % |
|
Recoflex |
16.6 mm |
16.7 mm |
100.6% |
< 0.6% |
|
MDF panel |
19.3 mm |
23.3 mm |
120.7% |
20.7% |
|
Particle board |
19.0 mm |
|
Breaking strength test |
|
| Material: |
Recoflex 16 mm, veneered on both sides |
| Type of test |
3-point bending tests |
| Support width: | 380 mm |
| Test standard | EN 3310 |
| Test velocity | 20 mm/min |
Compare particle board 19 mm = E module 2.000 N/mm²
Compare MDF panel = E module 2.200 N/mm²
|
t |
b |
Breaking force |
Resistance to bending |
E module |
t test |
Veneer thickness |
|
mm |
mm |
N |
N/mm² |
N/mm² |
s |
mm |
|
19.3 |
50.0 |
508 |
15.5 |
2354 |
37 |
1.4 |
|
18.4 |
49.7 |
556 |
18.8 |
2661 |
40 |
1.4 |
|
18.5 |
49.7 |
516 |
17.4 |
2685 |
37 |
1.4 |
|
20.1 |
50.0 |
778 |
21.9 |
2583 |
52 |
2.4 |
|
20.1 |
49.8 |
811 |
23.0 |
2838 |
53 |
2.4 |
|
20.2 |
50.3 |
833 |
23.2 |
2744 |
56 |
2.4 |
|
16.8 |
49.6 |
292 |
11.9 |
1648 |
37 |
0.5 laminated |
|
16.7 |
50.2 |
267 |
10.9 |
1634 |
33 |
0.5 laminated |
|
16.7 |
50.2 |
264 |
10.8 |
1602 |
34 |
0.5 laminated |
|
17.1 |
50.2 |
218 |
8.5 |
1762 |
20 |
0.5 |
|
17.3 |
50.3 |
211 |
8.0 |
1675 |
20 |
0.5 |
|
17.1 |
50.4 |
254 |
9.8 |
1709 |
27 |
0.5 |
|
Permanent impression following static load |
according to CATAS, Italy |
|
|
Recoflex unplanked |
3.2 mm |
EN 433/94 |
|
Permanent impression following static load, Recoflex planked on both sides with HPL plastic laminate |
0.06 mm |
EN 433/94 |
|
Permanent impression following static load, Recoflex planked on both sides with wood veneer |
0.16 mm |
EN 433/94 |